TECHNOLOGY
- Crystallization and Melting of Nylon 610
- Nylon 610/Graphene Oxide Composites Prepared by In-Situ Inte
- Preparation and properties of nylon-1010/montmorillonite nan
- Thermal properties and morphology of crystal in nylon 1010
- Difference between NYLON 6, NYLON 66, NYLON 11 and NYLON12
- PA1012 is used for extrusion coating.
NEWS
- Drug transport across nylon 610 films: influence of synthesi
- Spherulites in nylon 610 and nylon 66
- Special material for fishing line production - nylon PA612 drawing grade product
- Extrusion grade nylon PA12 raw material for tennis racket sheath
- High toughness, high impact strength and high abrasion resistance resin PA612 is used to make brushe
- Nylon 612 has good abrasion resistance and is used to make hoses
- PA610 is used to make high impact strength and high toughness bushings
TECHNOLOGY >>
PA1012 is used for extrusion coating.
PA1012 is used for extruding oil pipes, gas pipes and pipeline covering.
The parameters are as follows:
PA610 Resin PA612 Resin PA1010 Resin PA1212 Resin WECHAT：18602297376
| 性能名称 Test Item |
测试方法条件 Testing Standard |
单位 Units |
典型值 Value |
| 密度 Density |
ISO 1183 | g/cm3 | 1.04 |
| 拉伸强度 Tensile Strength |
ISO 527-1/-2 | Mpa | 55 |
| 断裂伸长率 Nominal strain at break |
ISO 527-1/-2 | % | >100 |
| 弯曲强度 Flexural Strength |
ISO 527-1/-2 | Mpa | 20 |
| 弯曲模量 Flexural Module |
ISO 527-1/-2 | MPa | 500 |
| 简支梁冲击强度 Charpy impact strength |
ISO 179 | KJ/m2 | N |
| 简支梁缺口冲击强度 Charpy notched impact strength |
ISO 179 | KJ/m2 | 4 |
| 熔点 Meling point |
ISO 3146 | ℃ | 190 |
| 热变形温度 Heat Deflection Temperation |
ISO 75-1/-2 | ℃ | 80 |